Chemische Zusammensetzung
Klasse |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Ti |
N |
Cu |
Nb |
201 |
≤0.15 |
≤1.0 |
5,50-7,50 |
≤0.05 |
≤0.03 |
16.00-18.00 |
3,50-5,50 |
- |
- |
0,05-0,25 |
- |
- |
202 |
≤0.15 |
≤1.0 |
7,50-10,00 |
≤0.05 |
≤0.03 |
17.00-19.00 |
4,00-6,00 |
- |
- |
0,05-0,25 |
- |
- |
301 |
≤0.15 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
16.00-18.00 |
6,00-8,00 |
- |
- |
≤0.1 |
- |
- |
302 |
≤0.15 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
8.00-10.00 |
- |
- |
≤0.1 |
- |
- |
303 |
≤0.15 |
≤1.0 |
≤2.0 |
≤0.2 |
≥0.15 |
17.00-19.00 |
8.00-10.00 |
≤0.6 |
- |
≤0.1 |
- |
- |
304 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
8.00-10.00 |
- |
- |
- |
- |
- |
304L |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
8.00-10.00 |
- |
- |
- |
- |
- |
304H |
0,04-0,1 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
8.00-10.00 |
- |
- |
- |
- |
- |
304N |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
8.00-10.00 |
- |
- |
0,10-0,16 |
- |
- |
304J1 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
6,00-9,00 |
- |
- |
- |
1,00-3,00 |
- |
305 |
≤0.12 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
10,50-13,00 |
- |
- |
- |
- |
- |
309S |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
22,00-24,00 |
12,00-15,00 |
- |
- |
- |
- |
- |
310S |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
24,00-26,00 |
19.00-22.00 |
- |
- |
- |
- |
- |
316 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
- |
- |
- |
- |
316L |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
12,00-15,00 |
2.00-3.00 |
- |
- |
- |
- |
316H |
≤0.1 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
- |
- |
- |
- |
316N |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
- |
0,10-0,16 |
- |
- |
316Ti |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
16.00-19.00 |
11.00-14.00 |
2.00-3.00 |
≥5C |
- |
- |
- |
317L |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
18.00-20.00 |
11.00-15.00 |
3,00-4,00 |
- |
- |
- |
- |
321 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
9.00-12.00 |
- |
5C-0,7 |
- |
- |
- |
347 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
9.00-12.00 |
- |
- |
- |
- |
10C-1.10 |
347H |
≤0.1 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
9.00-12.00 |
- |
- |
- |
- |
8C-1,10 |
2205 |
≤0.03 |
≤1.0 |
≤2.0 |
≤0.035 |
≤0.03 |
21,00-24,00 |
4,50-6,50 |
2,50-3,50 |
- |
0,08-0,20 |
- |
- |
2507 |
≤0.03 |
≤0.8 |
≤1.2 |
≤0.035 |
≤0.02 |
24,00-26,00 |
6,00-8,00 |
3,00-5,00 |
- |
0,24-0,32 |
- |
- |
904L |
≤0.02 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
19,00-23,00 |
23,00-28,00 |
4,00-5,00 |
- |
- |
1,00-2,00 |
- |
C276 |
≤0.02 |
≤0.05 |
≤1.0 |
- |
- |
14,00-16,50 |
Andere |
- |
- |
- |
- |
- |
Monel400 |
≤0.3 |
≤0.5 |
≤2.0 |
- |
≤0.024 |
- |
≥63 |
- |
- |
- |
28-34 |
- |
409L |
≤0.03 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
17.00-19.00 |
- |
- |
- |
- |
- |
- |
410 |
≤0.15 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
11,50-13,50 |
- |
- |
- |
- |
- |
- |
410L |
≤0.03 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
11,50-13,50 |
- |
- |
- |
- |
- |
- |
420J1 |
0,16-0,25 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
12.00-14.00 |
- |
- |
- |
- |
- |
- |
420J2 |
0,26-0,40 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
12.00-14.00 |
- |
- |
- |
- |
- |
- |
430 |
≤0.12 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
- |
- |
- |
- |
- |
436L |
≤0.025 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-19.00 |
- |
- |
- |
- |
- |
- |
439 |
≤0.03 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
- |
- |
- |
- |
- |
440A |
0,60-0,75 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
≤0.75 |
- |
- |
- |
- |
440B |
0,75-0,95 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
≤0.75 |
- |
- |
- |
- |
440C |
0,95-1,2 |
≤1.0 |
≤1.0 |
≤0.035 |
≤0.03 |
16.00-18.00 |
- |
≤0.75 |
- |
- |
- |
- |
441 |
≤0.03 |
0,2-0,8 |
≤0.7 |
≤0.03 |
≤0.015 |
17,50-18,50 |
- |
≤0.5 |
0,1-0,5 |
≤0.025 |
- |
0,3 + 3C-0.9 |